Scanning tunnelling microscopy (STM) was used to characterise the basal surface of fresh cleaved crystals of 2H-WS2. Although no impurity or stacking faults could be detected by X-ray diffraction, STM images obtained with negative bias voltage showed two kinds of defects. These defects were attributed to an iodine derivative used as transport agent. In a flat surface free of defects, an image with atomic resolution was achieved with sulphur distances and angles as expected for hexagonal symmetry of 2H-WS2.