Estructura cristalina y propiedades de la solución sólida YCoXMn1-XO3

Show simple item record

dc.contributor Comisión Interministerial de Ciencia y Tecnología, CICYT (España)
dc.creator Gutiérrez, D.
dc.creator Peña, Octavio
dc.creator Fernández Lozano, José Francisco
dc.creator Moure Jiménez, Carlos
dc.date 2008-06-02T09:47:29Z
dc.date 2008-06-02T09:47:29Z
dc.date 2002-01
dc.date.accessioned 2017-01-31T01:31:44Z
dc.date.available 2017-01-31T01:31:44Z
dc.identifier Boletín de la Sociedad Española de Cerámica y Vidrio 41(1): 137-142 (2002)
dc.identifier 0366-3175
dc.identifier http://hdl.handle.net/10261/4711
dc.identifier.uri http://dspace.mediu.edu.my:8181/xmlui/handle/10261/4711
dc.description [ES] Se han estudiado las soluciones sólidas correspondientes al sistema YCoXMn1-XO3 con x=0.2...0.7. Los polvos fueron preparados por reacción en estado sólido de los correspondientes óxidos. Se obtuvieron cerámicas sinterizadas densas por sinterización entre 1250º y 1350ºC. La incorporación de ~25 átomos % de Co a la manganita de itrio induce la aparición de una fase de tipo perovsquita, con simetría ortorrómbica y Grupo Espacial (G.E.) Pbnm, que se extiende al menos hasta valores de x=0.70. El aumento del contenido de Co desde x=0.25 hastax=0.70 lleva a un decrecimiento monótono del factor de ortorrombicidad b/a. Las medidas eléctricas han demostrado el comportamiento semiconductor de todas las soluciones sólidas con estructura de perovsquita. La conductividad a temperatura ambiente aumenta con Co hasta un valor de x=0.33 para después decrecer para mayores contenidos. La composición 60/40, Co/Mn muestra un aumento de la conductividad y una subsecuente disminución de la energía de activación respecto de la composición 50/50, Co/Mn. Un mecanismo de salto de pequeño polarón térmicamente activado controla la conducción de estas soluciones sólidas.
dc.description [EN] Solid solutions corresponding to the YCoXMn1-XO3 system, x=0.2...0.7 have been studied. The powders were prepared by solid state reaction of the corresponding oxides. Sintered bodies were obtained by firing between 1250 and 1350ºC. The incorporation of 25 at% Co2+ to the yttrium manganite induces the appearance of a perovskite-type phase with orthorhombic symmetry and Space Group Pbnm, which is extended at least up to an amount of x=0.70. Increase of the Co content from x=0.25 to x=0.70 leads to a monotonic decrease of the orthorhombicity factor b/a. Electrical measurements have shown semiconducting behaviour for all the solid solutions with the perovskite-type structure. The room temperature conductivity increases with Co up to x=0.33, and then decreases. The 60/40 Co/Mn composition shows an increase of the electrical conductivity respect to the 50/50 and a correlative decrease of the activation energy. Small polaron hopping mechanism thermally activated controls the conductivity of these ceramics.
dc.description Este trabajo ha sido financiado por CICYT-MAT-97-0679- C02-01.
dc.description Peer reviewed
dc.format 459424 bytes
dc.format application/pdf
dc.language spa
dc.publisher Sociedad Española de Cerámica y Vidrio
dc.relation http://boletines.secv.es/es/index.php?id=42&vol=41
dc.rights openAccess
dc.subject Manganitas
dc.subject Soluciones sólidas de perovsquitas
dc.subject Cerámicas
dc.subject Propiedades eléctricas
dc.subject Manganites
dc.subject Perovskite solid solutions
dc.subject Electrical properties
dc.subject Ceramics
dc.title Estructura cristalina y propiedades de la solución sólida YCoXMn1-XO3
dc.title Crystalline structure and electrical properties of YCoxMn1-xO3 solid soluitons
dc.type Artículo


Files in this item

Files Size Format View

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record

Search DSpace


Advanced Search

Browse

My Account