[EN] Strontium cerate is the parent phase of an important class of proton-conducting perovskites with various potential technological
applications. Phase formation and structure of SrCeO3 with Sr:Ce nonstoichiometry have been investigated for the
series, Sr1±xCeO3±δ (0.98 ≤ x ≤ 1.04). Analyses by EPMA (electron probe micro analysis) and X-ray diffraction (XRD) indicate
that, for samples sintered at 1350°C, the main phase is Sr-rich for all x. The accommodation of excess SrO in the bulk phase
and/or intergranular regions is discussed. The stability of nominally stoichiometric SrCeO3 was examined in an atmosphere
of high water vapour partial pressure (pH2O) for 2 hours, degrading to Sr(OH)2.H2O and CeO2 for pH2O ≥ 3.6atm.
[ES] La fase SrCeO3 da origen a una importante familia de perovskitas conductoras protónicas con potenciales aplicaciones tecnológicas.
En este trabajo se estudia la formación de la fase y la estructura de SrCeO3 con la relación Sr:Ce no estequiométrica
para la serie Sr1±xCeO3±δ (0.98 ≤ x ≤ 1.04). Los análisis por microsonda (EPMA) y difracción de rayos X (DRX) indican que en
las muestras sinterizadas a 1350°C, la fase principal es rica en estroncio para todo valor de x. Se discute la posible ubicación
del exceso de SrO tanto en la región intergranular como en el propio grano. También se examina la estabilidad de la composición
con estequiometría nominal SrCeO3 en una atmosfera con una alta presión de vapor de agua (pH2O), observándose
que la degradación a Sr(OH)2.H2O y CeO2 ocurre a pH2O ≥ 3.6atm (expuesto durante 2 horas).
One of the authors (GCM) is sponsored by the EU RTN
programme High Temperature Proton Conductors (HiTP)
“Investigation of high temperature solid proton conductors
of relevance to fuel processing and energy conversion applications”.
Peer reviewed