| dc.creator |
Pena, Pilar |
|
| dc.creator |
Vargas Gutiérrez, G. |
|
| dc.creator |
López-Cuevas, J. |
|
| dc.creator |
Méndez Nonell, J. |
|
| dc.creator |
Vázquez, F. |
|
| dc.creator |
Méndez, M. |
|
| dc.date |
2008-05-29T09:50:15Z |
|
| dc.date |
2008-05-29T09:50:15Z |
|
| dc.date |
2004-01 |
|
| dc.date.accessioned |
2017-01-31T01:29:55Z |
|
| dc.date.available |
2017-01-31T01:29:55Z |
|
| dc.identifier |
Boletín de la Sociedad Española de Cerámica y Vidrio 43(1): 71-74 (2004) |
|
| dc.identifier |
0366-3175 |
|
| dc.identifier |
http://hdl.handle.net/10261/4638 |
|
| dc.identifier.uri |
http://dspace.mediu.edu.my:8181/xmlui/handle/10261/4638 |
|
| dc.description |
[ES] Se analiza el efecto de la aplicación de las microondas durante 1,5 minutos sobre el cambio de volumen, porosidad y conductividad térmica
de probetas de silicato de sodio/wollastonita. Se han estudiado mezclas con 20 a 100 % de silicato de sodio1. Se obtuvo una pérdida en masa
del 19 % y un incremento de volumen del 50 % en mezclas con 20 % de silicato de sodio. A medida que el contenido de éste aumentó, la pérdida
en masa se incrementó hasta 27 % y el cambio de volumen hasta en 500 % para probetas con 100 % de silicato de sodio. Se obtuvieron
espumas cerámicas con porosidades totales de 65 % en probetas con 20 % de silicato de sodio (densidades aparente de 1,0 y real de 2,75 g/cc)
y de 91 % en muestras con 100 % de silicato de sodio (densidades aparente de 0,182 y real de 2,0 g/cc). El tamaño de poro más uniforme se
obtuvo para contenidos del 80 % de silicato de sodio (10 a 30 μm). Las conductividades térmicas de las espumas cerámicas fueron de 0,2, 0,125
y 0,065 W/m·K para contenidos de 40, 70 y 100 % de silicato de sodio, respectivamente. |
|
| dc.description |
[EN] The effect of the application of microwaves on the volume, porosity and thermal conductivity of sodium silicate-wollastonite mixtures was
studied. The compositional range studied was 20-100 wt% sodium silicate. A weight loss of 19% and a volume increase of 50% were obtained
for mixtures with 20 wt% sodium silicate. The weight loss increased up to 27% with increasing sodium silicate content. Volume increased in
500% for samples with 100 wt% sodium silicate. Ceramic foams with total porosities of 65 vol % were obtained for specimens containing 20
wt% sodium silicate (with apparent and real densities of 1.0 and 2.75 g/cc, respectively), while samples containing 100 wt% sodium silicate
presented total porosities of 91 vol% (with apparent and real densities of 0.182 and 2.0 g/cc, respectively). The best pore size uniformity (10-30
μm) was obtained for a sodium silicate content of 80 wt%. The thermal conductivities of the ceramic foams were 0.2, 0,125 and 0,065 W/m·K
for sodium silicate contents of 40, 70 and 100 wt%, respectively. |
|
| dc.description |
Peer reviewed |
|
| dc.format |
447921 bytes |
|
| dc.format |
application/pdf |
|
| dc.language |
spa |
|
| dc.publisher |
Sociedad Española de Cerámica y Vidrio |
|
| dc.relation |
http://boletines.secv.es/es/index.php?id=17&vol=43 |
|
| dc.rights |
openAccess |
|
| dc.subject |
Espumas cerámicas |
|
| dc.subject |
Microondas |
|
| dc.subject |
Silicatos |
|
| dc.subject |
Ceramic foams |
|
| dc.subject |
Microwaves |
|
| dc.subject |
Silicates |
|
| dc.title |
Espumado de mezclas de silicato de sodio-wollastonita por microondas |
|
| dc.title |
Foaming of sodium silicate-wollastonite mixtures by microwaves |
|