| dc.creator |
Auger, M. A. |
|
| dc.creator |
Sánchez, O. |
|
| dc.creator |
Albella, J. M. |
|
| dc.date |
2008-05-27T07:12:32Z |
|
| dc.date |
2008-05-27T07:12:32Z |
|
| dc.date |
2004-03 |
|
| dc.date.accessioned |
2017-01-31T01:27:46Z |
|
| dc.date.available |
2017-01-31T01:27:46Z |
|
| dc.identifier |
Boletín de la Sociedad Española de Cerámica y Vidrio 43(2): 488-490 (2004) |
|
| dc.identifier |
0366-3175 |
|
| dc.identifier |
http://hdl.handle.net/10261/4534 |
|
| dc.identifier.uri |
http://dspace.mediu.edu.my:8181/xmlui/handle/10261/4534 |
|
| dc.description |
[ES] En este trabajo se han estudiado láminas de TiN crecidas sobre cuchillas de acero inoxidable empleadas en el corte de fibra de vidrio, para
mejorar sus propiedades mecánicas y aumentar el tiempo de vida de la herramienta, reduciendo de este modo las paradas de producción. La
técnica de depósito utilizada ha sido la de sputtering magnetrón reactivo. La composición química de las capas de TiN ha sido determinada
mediante medidas de Espectroscopía Auger, RBS (Rutherford Backscattering Spectroscopy) y XANES (X-Ray Spectroscopy Near the
Absorption Edge) y se ha relacionado con la composición de la mezcla gaseosa presente en la cámara de reacción. La estructura cristalina
se ha determinado mediante Difracción de Rayos X, y mediante la técnica de SEM (Scanning Electron Microscopy) se ha observado la
morfología de las capas. La dureza del recubrimiento se ha calculado a partir de medidas de nanoindentación, obteniéndose un valor de
21.54±1.04 GPa, típico en la literatura para el TiN. Los resultados de la prueba en fábrica de las cuchillas recubiertas muestran un aumento
en su tiempo de vida de hasta un 67%. |
|
| dc.description |
[EN] TiN coatings on stainless steel blades for glass fibre cutting have been investigated in this work. The aim was to improve their mechanical
properties and increase the tool time life, decreasing in this way the production stops. Reactive magnetron sputtering has been the deposition
technique. TiN films chemical composition has been determined by AES (Auger Electron Spectroscopy), RBS (Rutherford Backscattering
Spectroscopy) and XANES (X-Ray Spectroscopy Near the Absorption Edge), and it has been correlated to the gas mixture composition in
the vacuum chamber. Crystalline structure has been determined by X-Ray Diffraction, and the films morphology has been observed by SEM
(Scanning Electron Microscopy). The hardness coating has been extracted from nanoindentation measurements, giving a 21.54±1.04 GPa
hardness value, typical for TiN in the literature. Factory proofs for coated cutting blades show a 67% lifetime increase. |
|
| dc.description |
La realización de este trabajo ha sido posible gracias a la financiación del proyecto PETRI (R-PETRI PTR1995-0416-OP-02-01), en colaboración con la Fundación TEKNIKER y la Empresa VETROTEX
España. |
|
| dc.description |
Peer reviewed |
|
| dc.format |
237392 bytes |
|
| dc.format |
application/pdf |
|
| dc.language |
spa |
|
| dc.publisher |
Sociedad Española de Cerámica y Vidrio |
|
| dc.relation |
http://boletines.secv.es/es/index.php?id=18&vol=43 |
|
| dc.rights |
openAccess |
|
| dc.subject |
Sputtering magnetrón reactivo |
|
| dc.subject |
TiN |
|
| dc.subject |
Propiedades mecánicas |
|
| dc.subject |
Dureza |
|
| dc.subject |
Reactive magnetron sputtering |
|
| dc.subject |
Mechanical properties |
|
| dc.subject |
Hardness |
|
| dc.title |
Depósito de TiN sobre herramientas de corte para uso industrial |
|
| dc.title |
TiN deposition on cutting tools for industrial use |
|