[EN] Vitreous cylinders with compositions Bi2-xPbxSr2CaCu2Oy, (x = 0, 0.2, 0.4 and 0.6) were prepared and used as precursors to fabricate textured bars through a laser floating zone melting method (LFZ). The resulting textured cylindrical bars were annealed, followed by their electrical characterization. The microstructure was determined and correlated with the electrical measured properties. The influence of Pb doping on the sharpness of the superconducting to normal transition on the E-I curves has been determined. The sharpest transitions have been obtained for samples doped with 0.4Pb.[ES] Se han preparado precursores de tipo vítreo en forma de cilindro con composiciones nominales Bi2-xPbxSr2CaCu2Oy, con x = 0, 0.2, 0.4 y 0.6. Estos cilindros se han utilizado como precursores para fabricar barras texturadas por medio de una técnica de fusión zonal inducida por láser (LFZ). Estas barras texturadas se recocieron a diferentes temperaturas y se caracterizaron eléctricamente. Además, se examinó su microestructura para correlacionarla con las propiedades eléctricas medidas. La variación de la transición del estado superconductor al normal se ha relacionado con el dopaje con Pb a través de las curvas E-I. Las mejores transiciones se han obtenido para muestras dopadas con 0.4 Pb.The authors wish to thank the Spanish Ministry of Science and Technology (MCyT, MAT 2002-04121-C03-02) and the Gobierno de Aragón (Consolidated Research Groups E03 and T12) for financial support.Peer reviewed