| dc.contributor |
Comisión Interministerial de Ciencia y Tecnología, CICYT (España) |
|
| dc.creator |
Soriano, David |
|
| dc.creator |
Mazo Fernández, María Alejandra |
|
| dc.creator |
Rubio Alonso, Fausto |
|
| dc.creator |
Rubio Alonso, Juan |
|
| dc.creator |
Oteo Mazo, José Luis |
|
| dc.date |
2008-05-05T10:55:02Z |
|
| dc.date |
2008-05-05T10:55:02Z |
|
| dc.date |
2006-11 |
|
| dc.date.accessioned |
2017-01-31T01:09:50Z |
|
| dc.date.available |
2017-01-31T01:09:50Z |
|
| dc.identifier |
Boletín de la Sociedad Española de Cerámica y Vidrio 45(6): 379-388 (2006) |
|
| dc.identifier |
0366-3175 |
|
| dc.identifier |
http://hdl.handle.net/10261/3994 |
|
| dc.identifier.uri |
http://dspace.mediu.edu.my:8181/xmlui/handle/10261/3994 |
|
| dc.description |
[ES] En este trabajo se ha estudiado la degradación térmica de nanocomposites resol-alcóxido (TEOS o APS) preparados mediante
el proceso sol-gel. Esta degradación se ha caracterizado tanto mediante estudios cinéticos (Energía de Activación, orden de
reacción y factor pre-exponencial) como por estudios degradativos (IPDT, IDT). En todos los casos la base de estudio han
sido los termogramas realizados a distintas velocidades. Los valores de las energías de activación encontrados han sido
similares a nanocomposites recogidos en la bibliografía (con valores comprendidos entre 100 y 200 kJ.mol-1). Por otro lado,
los órdenes de reacción han estado comprendidos entre 1,5 y 3,0 dependiendo del método utilizado y del nanocomposite
analizado. Los valores de IPDT para todos los nanocomposites han sido superiores a 500 ºC llegando en algunos casos
a los 650 ºC. Finalmente se han calculado los valores del tiempo de vida media para una temperatura de 505 ºC y una
degradación del 95% del nanocomposite, habiéndose alcanzado valores superiores a los 1100 minutos. Todos estos resultados
se han correlacionado con los espectros IR en los que se ha observado que las mayores resistencias se alcanzan en aquellos
nanocomposites en los que la resina interacciona con las partículas del alcóxido. |
|
| dc.description |
[EN] The thermal degradation of TEOS-resol and APS-resol nanocomposites prepared by the sol-gel process has been studied in
this work. Kinetic studies based on activation energies, reaction orders and pre-exponential factors as well as degradation
analysis based on IPDT and IDT have been used in this work. For such studies thermograms at different heating velocities
have been used. Activation energies between 100 and 200 kJ.mol-1 have been obtained in this work. Such values are of the
same order as those found in the literature. On the other hand reaction orders vary between 1,5 and 3,0, depending on
the nanocomposite analysed and the procedure used. At the same time IPDT values have been always higher than 500 ºC
reaching values close to 650 ºC in some cases. Finally half life times calculated at a degradation temperature of 505 ºC and
conversions of 95% have reached 1100 minutes for the best nanocomposites. All of these results have been correlated with
IR spectra showing that those nanocomposites where resol molecules react with hydrolysed TEOS or APS they give the high
degradation resistance. |
|
| dc.description |
Este trabajo ha sido realizado dentro de un proyecto financiado por la Comisión Interministerial de Ciencia y Tecnología de España (CICYT, Proyecto Ref. MAT2002-03891). |
|
| dc.description |
Peer reviewed |
|
| dc.format |
1490897 bytes |
|
| dc.format |
application/pdf |
|
| dc.language |
spa |
|
| dc.publisher |
Sociedad Española de Cerámica y Vidrio |
|
| dc.relation |
http://boletines.secv.es/es/index.php?id=9&vol=45 |
|
| dc.rights |
openAccess |
|
| dc.subject |
Nanocomposites |
|
| dc.subject |
Resol |
|
| dc.subject |
TEOS |
|
| dc.subject |
APS |
|
| dc.subject |
Degradación térmica |
|
| dc.subject |
Cinética |
|
| dc.subject |
Thermal degradation |
|
| dc.subject |
Kinetics |
|
| dc.title |
Degradación térmica de nanocomposites TEOS/resol y γ-APS/resol |
|
| dc.title |
Thermal degradation of TEOS/resol and γ-APS/resol nanocomposites |
|
| dc.type |
Artículo |
|