| dc.contributor |
Comisión Interministerial de Ciencia y Tecnología, CICYT (España) |
|
| dc.contributor |
Ministerio de Educación y Ciencia (España) |
|
| dc.creator |
Lara, C. |
|
| dc.creator |
Pascual, M. Jesús |
|
| dc.creator |
Durán, Alicia |
|
| dc.date |
2008-05-05T09:40:23Z |
|
| dc.date |
2008-05-05T09:40:23Z |
|
| dc.date |
2007-03 |
|
| dc.date.accessioned |
2017-01-31T01:09:40Z |
|
| dc.date.available |
2017-01-31T01:09:40Z |
|
| dc.identifier |
Boletín de la Sociedad Española de Cerámica y Vidrio 46(2): 62-70 (2007) |
|
| dc.identifier |
0366-3175 |
|
| dc.identifier |
http://hdl.handle.net/10261/3989 |
|
| dc.identifier.uri |
http://dspace.mediu.edu.my:8181/xmlui/handle/10261/3989 |
|
| dc.description |
[ES] Los vidrios de composición molar 50SiO2•30BaO•20ZnO (Zn1.5-50), 55SiO2•27BaO•18ZnO (Zn1.5-55), y
55SiO2•27BaO•18MgO (Mg1.5-55) presentan buenas propiedades para su aplicación en el sellado de pilas de combustible de óxido sólido de configuración plana y temperatura de operación intermedia (850ºC) (IT-SOFC). El sellado debe
producirse a través de la sinterización del polvo de vidrio, durante el arranque de la pila, a temperaturas entre 700 y 850ºC. El tratamiento posterior a la temperatura de operación da lugar a la cristalización de silicatos de bario con el consiguiente aumento de viscosidad y rigidez del sello. Este trabajo es un estudio del comportamiento de sinterización de estos vidrios utilizando diferentes velocidades de
calentamiento y distribuciones de tamaño de partícula del polvo de vidrio, para la obtención final de sellos densos y homogéneos. Los vidrios Zn1.5-55 y Mg1.5-55 con un tamaño de partícula <63 μm y tratados a 2ºC/min alcanzan densidades finales superiores al 95%. Por otra parte, se ha demostrado el buen acuerdo entre las cinéticas de densificación obtenidas experimentalmente y las predichas por el modelo de sinterización de formación de Clusters en ausencia de
cristalización concurrente. |
|
| dc.description |
[EN] Glasses of composition 50SiO2•30BaO•20ZnO, mol% (Zn1.5-50), 55SiO2•27BaO•18ZnO, mol% (Zn1.5-55), and 55SiO2•27BaO•18MgO, mol% (Mg1.5-55) present good properties for application in sealing planar solid oxide fuel cells with an intermediate temperature of operation (850ºC) (IT-SOFC). The sealing must take place on sintering the glass powder during the start-up of the cell between 700 and 850ºC. Further treatment at the operation temperature provokes
the crystallisation of barium silicates with the subsequent increase of viscosity and seal rigidity. This work is a study of the sintering behaviour of these glasses using different heating rates and particle-size distributions
of the glass powder in order to obtain dense and homogeneous seals. The glasses Zn1.5-55 and Mg1.5-55 with a particle size <63 μm heated at 2ºC/min reach final densities higher than 95%. A good agreement has been demonstrated between
the measured sintering kinetics and those predicted with the sintering model of Clusters formation in the absence of concurrent crystallisation. |
|
| dc.description |
Este trabajo ha sido financiado por el proyecto CICYT MAT2006-04375 y el programa Ramón y Cajal del Ministerio de Educación y Ciencia (MEC). |
|
| dc.description |
Peer reviewed |
|
| dc.format |
1535859 bytes |
|
| dc.format |
application/pdf |
|
| dc.language |
spa |
|
| dc.publisher |
Sociedad Española de Cerámica y Vidrio |
|
| dc.relation |
http://boletines.secv.es/es/index.php?id=23&vol=46 |
|
| dc.rights |
openAccess |
|
| dc.subject |
Vitrocerámicos |
|
| dc.subject |
Sinterización |
|
| dc.subject |
SOFC |
|
| dc.subject |
Sellado |
|
| dc.subject |
Glass-ceramics |
|
| dc.subject |
Sintering |
|
| dc.subject |
Sealing |
|
| dc.title |
Sinterización de vidrios del sistema RO-BaO-SiO2 (R= Mg, Zn) para el sellado de SOFC |
|
| dc.title |
Sintering of glasses in the system RO-BaO-SiO2 (R= Mg, Zn) for sealing SOFC |
|
| dc.type |
Artículo |
|