FCC catalyst is made up of particles of complex composition where the main active component is a Y zeolite. This work presents the textural and structural results of a commercial USY zeolite which had been previously prepared from a set of catalysts with 7, 15, 25, 35 y 45% of active material and of the hydrothermally deactivated materials zeolite. The samples have been characterized by X-ray fluorescence (XRF), X-ray diffraction (XRD), 29Si NMR spectroscopy and nitrogen adsorption at 77K. From these results was found correlations between micropore volume and zeolite content and degree crystallinity and %zeolite. Also, it was found that an hydrothermal treatment at 1033 K with only 20% steam during 16 hours destroys the structural groups Si(2Al) and Si(3Al) as a reflection of the strongly dealumination of the zeolite component of the catalyst.El catalizador de FCC está constituido por partículas de composición compleja donde el componente activo es una zeolita Y. En este trabajo se presentan los resultados texturales y estructurales de una zeolita USY comercial lixiviada, de una serie de catalizadores con 7, 15, 25, 35 y 45% de material activo y los de estos materiales desactivados hidrotérmicamente. Las muestras se caracterizaron por fluorescencia de rayos X (FRX), difracción de rayos X (DRX), resonancia magnética nuclear de silicio (29Si RMN) y fisiadsorción de nitrógeno a 77 K. A partir de estos resultados se hallaron correlaciones entre el volumen de microporo y el contenido de zeolita y entre el grado de cristalinidad y el porcentaje de zeolita. Además, se encontró que un tratamiento con sólo 20% de vapor de agua a 1033 K durante 16 horas destruye los grupos estructurales Si(2Al) y Si(3Al) como reflejo de la dealuminización drástica que sufre el material.Los autores agradecen al Instituto Colombiano del Petróleo por el suministro de la zeolita USY y el "caolín clay" y a la Universidad Nacional de Colombia por el soporte financiero.Peer reviewed